Transparent mesoporous silica coatings were achieved by conventional sol-gel process. The obtained coatings display permanent supra- amphiphilicity, transparent appearance and good wetting property with very fast spread rate. Incorpo- ration of functional materials such as crystalline tita- nia nanoparticles into the coatings was also carried out without affecting the transparency and supra- amphiphilicity.
Transparent mesoporous silica coatings were achieved by conventional sol-gel process. The obtained coatings display permanent supraamphiphilicity, transparent appearance and good wetting property with very fast spread rate. Incorporation of functional materials such as crystalline titania nanoparticles into the coatings was also carried out without affecting the transparency and supraamphiphilicity.
基金
The authors would like to thank Prof.Jiang Lei and Dr.Feng Lin of Institute of Chemistry,Chinese Academy of Sciences for the measurement of contact angles.This work was supported by the National Natural Science Foundation of China(Grant Nos.50573083,50325313,90206025 and 20128004)
the Chinese Academy of Sciences and the China Ministry of Science and Technology(Grant Nos.2004-01-09,2003CB615600 and KJCX2-SW-H07).