CaSiO3：Eu0.08^3＋Bi0.002^3＋ with a monoclinic perovskite structure was synthesized by using sol-gel method, and its luminescence characteristics were investigated. From the excitation spectrum, it can be seen that the main peaks located at 238,396,415,437 and 359 nm correspond to the charge-transfer band of Eu^3＋-O^2- , the absorption transitions of ^7F0.1→^3L6, ^7F0→^5D3, ^7F1→^5D3 of Eu^3＋ ions, and ^3P1→^1S0 of Bi^3＋ ions, respectively. When the samples were excited with a light of wavelength 359 or 395 nm, it can be seen from the emission spectrum that the electronic dipole transition located at 609 nm corresponding to ^5D0→^7F2 of Eu^3＋ ions was stronger than the magnetic dipole transition located at 587 nm corresponding to ^5D0→^7F1 of Eu^3＋ ions, which shows that more Eu^3＋ ions were located in nonreversion center lattices. The energy transfer from Bi^3＋ ions to Eu^3＋ ions in the phosphor was also discussed. The results show that Eu^3＋ ions could be well sensitized by ^3＋ions, and the energy-transfer pattern between Bi^3＋ ions and Eu^3＋ ions was resonance energy transfer.
CaSiO3：Eu0.08^3＋Bi0.002^3＋ with a monoclinic perovskite structure was synthesized by using sol-gel method, and its luminescence characteristics were investigated. From the excitation spectrum, it can be seen that the main peaks located at 238,396,415,437 and 359 nm correspond to the charge-transfer band of Eu^3＋-O^2- , the absorption transitions of ^7F0.1→^3L6, ^7F0→^5D3, ^7F1→^5D3 of Eu^3＋ ions, and ^3P1→^1S0 of Bi^3＋ ions, respectively. When the samples were excited with a light of wavelength 359 or 395 nm, it can be seen from the emission spectrum that the electronic dipole transition located at 609 nm corresponding to ^5D0→^7F2 of Eu^3＋ ions was stronger than the magnetic dipole transition located at 587 nm corresponding to ^5D0→^7F1 of Eu^3＋ ions, which shows that more Eu^3＋ ions were located in nonreversion center lattices. The energy transfer from Bi^3＋ ions to Eu^3＋ ions in the phosphor was also discussed. The results show that Eu^3＋ ions could be well sensitized by ^3＋ions, and the energy-transfer pattern between Bi^3＋ ions and Eu^3＋ ions was resonance energy transfer.
基金
Supported by the State Key Basic Research Program of China(No. 2003CD314702-02)
Education Bureau of Jilin Province(No. 200318).