Yttrium-filled sku, tterudites Yy Fex Co4-x Sb12 （ Y =0- 0. 40 ） were synthesized. The effect of Y filling fraction on thermoelectric properties of Yy Fex Co4-x Sb12 was investigated. All samples showed p-type conduct. The electrical conductivity decreased with increasing filling fraction y. The Seebeck coefficient inreased with increasing temperature. The lattice thermal conductivity decreased with increasing filling fraction y and showed the minimum value at a certain filling fraction y = 0.3. The effect of different filling atoms M（ M： Ba, Ce, Y） on the lattice thermal conductivity of MyFexCo4-xSb12 was discussed. The maximum ZT value of O. 7 was obtained for Y0.06 Fe0.7 Co3.3 Sb12 at 750 K.
Yttrium-filled sku, tterudites Yy Fex Co4-x Sb12 （ Y =0- 0. 40 ） were synthesized. The effect of Y filling fraction on thermoelectric properties of Yy Fex Co4-x Sb12 was investigated. All samples showed p-type conduct. The electrical conductivity decreased with increasing filling fraction y. The Seebeck coefficient inreased with increasing temperature. The lattice thermal conductivity decreased with increasing filling fraction y and showed the minimum value at a certain filling fraction y = 0.3. The effect of different filling atoms M（ M： Ba, Ce, Y） on the lattice thermal conductivity of MyFexCo4-xSb12 was discussed. The maximum ZT value of O. 7 was obtained for Y0.06 Fe0.7 Co3.3 Sb12 at 750 K.
基金
Funded by National Natural Science Foundation of China (No.50372049)