摘要
To increase the adhesion strength between the coating and the substrate, sintered Ti（C,N）-based cermets were selected and deposited with monolayer TiN using a multiarc ion-plating technique; subsequently, hot isostatic pressing （HIPhag） treatment was performed at 1000℃ using nitrogen pressure up to 110 MPa. The mechanical properties of cermets after a coating process and subsequent HIPing treatment have been evaluated with respect to the hardness, the residual stress, and the coating adhesion. The results show that atter the HIPing process, there was a higher increase ha critical load ha the TiN-coated cermets with lower surface roughness compared with those with higher surface roughness. In all cases, the residual stress was found to be compressive. The effects of substrate surface roughness and posttreatment on the adhesion strength of the coatings were thus investigated. It was also fotmd that the HIPing posttreatment process is well suited for hacreasing the adhesion strength between the coating and the substrate.
To increase the adhesion strength between the coating and the substrate, sintered Ti（C,N）-based cermets were selected and deposited with monolayer TiN using a multiarc ion-plating technique; subsequently, hot isostatic pressing （HIPhag） treatment was performed at 1000℃ using nitrogen pressure up to 110 MPa. The mechanical properties of cermets after a coating process and subsequent HIPing treatment have been evaluated with respect to the hardness, the residual stress, and the coating adhesion. The results show that atter the HIPing process, there was a higher increase ha critical load ha the TiN-coated cermets with lower surface roughness compared with those with higher surface roughness. In all cases, the residual stress was found to be compressive. The effects of substrate surface roughness and posttreatment on the adhesion strength of the coatings were thus investigated. It was also fotmd that the HIPing posttreatment process is well suited for hacreasing the adhesion strength between the coating and the substrate.
基金
This work was financially supported by the National Natural Science Foundation of China (No. 50074017).