A new kind of phosphorus-containing monomer bis(4-(p-fluorobenzoyl)phenyl)phenylphosphine oxide was synthesized first,then a poly(aryl ether ketone) containing phosphorus in the main ring was synthesized,derived from bis(4-(p-fluorobenzoyl)phenyl)phenylphosphine oxide and bisphenol-S by nucleophilic copolycondensation with the use of sulfolane as solvent.The structure was confirmed by FT-IR,()31P-NMR and()1H-NMR.Electrical property,mechanical property,heat-resistance property,combustion-resistance and solubility was also researched to know the influence of the containing of phosphorus.The results showed that the polymer have excellent heat-resistance,the glass transition temperature(Tg) was 235℃.The onset temperature taken at 5% weight loss of the polymer in nitrogen was 463℃.The polymer was soluble in CH2Cl2,CHCl3,Cl2(CH)2Cl2,Cl(CH2)2Cl and strongly polar organic solvents such as(N,N-dimethylformamide)(DMF),N-methyl2pyrrolidone (NMP) at room temperature.
A new kind of phosphorus-containing monomer bis (4- (p-fluombenzoyl) phenyl)phenylphosphine oxide was synthesized first,then a poly(aryl ether ketone) containing phosphorus in the main ring was synthesized,derived from his (4-(p-fluorobenzoyl) phenyl)phenylphosphine oxide and bisphenol-S by nucleophilic copolycondensation with the use of sulfolane as solvent. The structure was confirmed by FT-IR, 31 P-NMR and ^1H-NMR. Electrical property, mechanical property, heat-resistance property, combustion-resistance and solubility was also researched to know the influence of the containing of phosphorus. The results showed that the polymer have excellent heatresistance, the glass transition temperature ( Tg ) was 235℃. The onset temperature taken at 5 % weight loss of the polymer in nitrogen was 463 ℃. The polymer was soluble in CH2 Cl2, CHCl3, Cl2 ( CH)2 Cl2, Cl( CH2 )2 Cl and strongly polar organic solvents such as N, N-dimethylformamide (.DMF), N-methyl-2-pyrrolidone (NMP) at room temperature.
出处
《高分子学报》
SCIE
CAS
CSCD
北大核心
2007年第1期90-92,共3页
Acta Polymerica Sinica
基金
国家自然科学基金(基金号50203008)资助项目
关键词
聚芳醚酮
含磷单体
双(4-(对氟苯甲酰基)苯基)苯基氧化膦
亲核取代
Poly ( aryl ether ketone), Phosphorus monomer, Bis ( 4-( p-formyl fluorobenz) phenyl phenylphosphine oxide, Nucleophilic substitution reaction