摘要
Nanocrystal of upconversion （UC） phosphor Ho^3＋, Tm^3＋ , and Yb^3＋ co-doped NaYF4 was prepared by the hydrothermal method in the presence of the complexing agent EDTA. Under 980 nm diode laser excitation, the impact of different concentrations of Ho^3＋ ion on the UC luminescence intensity was discussed. The law of luminescence intensity versus pump power shows that the 474 nm blue emission, 538 nm green emission, and 642 nm red emission are all due to the two-photon process, while the 450 nm blue emission is a three-photon process. The UC mechanism and processes were also analyzed. The sample was characterized by transmission electron microscopy （TEM） and X-ray diffraction （XRD）. The result shows that Ho^3＋ ,Tm^3＋ , and Yb^3＋ co-doped NaYF4 prepared by the hydrothermal method exhibits a hexagonal nanocrystal.
Nanocrystal of upconversion （UC） phosphor Ho^3＋, Tm^3＋ , and Yb^3＋ co-doped NaYF4 was prepared by the hydrothermal method in the presence of the complexing agent EDTA. Under 980 nm diode laser excitation, the impact of different concentrations of Ho^3＋ ion on the UC luminescence intensity was discussed. The law of luminescence intensity versus pump power shows that the 474 nm blue emission, 538 nm green emission, and 642 nm red emission are all due to the two-photon process, while the 450 nm blue emission is a three-photon process. The UC mechanism and processes were also analyzed. The sample was characterized by transmission electron microscopy （TEM） and X-ray diffraction （XRD）. The result shows that Ho^3＋ ,Tm^3＋ , and Yb^3＋ co-doped NaYF4 prepared by the hydrothermal method exhibits a hexagonal nanocrystal.
基金
Project supported bythe Key Laboratory of Rare Earth Chemistry and Physics ,ChangchunInstitute of Applied Chemistry ,Chinese Academy of Sciences (R020202K)