摘要
A series of novel Er^3＋/Yb^3＋ co-doped （85- x ） TeO2-15WO3-xB2O3 （TWB;x=2%,5%,8%（mole fraction） ） glasses were prepared. Influence of B203 on the spectroscopic properties of Er^3＋/Yb^3＋ co-doped tungsten-tellurite glasses were investigated. It is found that the intensity of 1.5μm fluorescence, lifetime of the ^4I13/2 level and upconversion fluorescence all decrease with the increase of B2O3 content. The product of full width at half maximum （FWHM） and stimulated emission cross-section （σe^peak） of Er^3＋ ：^4I13/2→^4I15/2 transition has an optimum when B203 is 5% （mole fraction）. The emission spectra of Er^3＋ ： ^4I13/2→^4I15/2 transition was analyzed using peak-fit routine, and an equivalent four-level system was proposed to estimate the stark splitting for the 411512 and ^4I13/2 levels of Er^3＋ ions in TWB glasses at room temperature.
A series of novel Er^3＋/Yb^3＋ co-doped （85- x ） TeO2-15WO3-xB2O3 （TWB;x=2%,5%,8%（mole fraction） ） glasses were prepared. Influence of B203 on the spectroscopic properties of Er^3＋/Yb^3＋ co-doped tungsten-tellurite glasses were investigated. It is found that the intensity of 1.5μm fluorescence, lifetime of the ^4I13/2 level and upconversion fluorescence all decrease with the increase of B2O3 content. The product of full width at half maximum （FWHM） and stimulated emission cross-section （σe^peak） of Er^3＋ ：^4I13/2→^4I15/2 transition has an optimum when B203 is 5% （mole fraction）. The emission spectra of Er^3＋ ： ^4I13/2→^4I15/2 transition was analyzed using peak-fit routine, and an equivalent four-level system was proposed to estimate the stark splitting for the 411512 and ^4I13/2 levels of Er^3＋ ions in TWB glasses at room temperature.
基金
Project supported bythe National Natural Science Foundation of Zhejiang Province (104498) ,the Foundation of Science andTechnology Bureau of Zhejiang Province (2005C31014 and 2006C21082)