研究ＧＣｒ１５钢丝在轧尖、冷拔时产生“搓衣板状”横裂纹缺陷的机理，指出控制好钢丝出炉淬水温度是防止横裂纹缺陷出现的具体办法。
o study the mechanism of cross cracks like washboard occurring in GCr15 steel wire during being pointed and cold drawn. It's pointed out that it can effectively prevent cross cracks from occurring to control well the water quench temperature of steel wire off the furnace.