The imidazole covalently coordinated sandwich-type heteropolymngstates Na9[ {Na（H=O2}3{M（C3H4N2）}3（ Sb W9O33）2]·xH=O（M=Ni^Ⅱ, Co^Ⅱ, Zn^Ⅱ, Mn^Ⅱ） were obtained by the reaction of Na2WO4·2H2O, SbCl3·6H2O, NiCl2·6H2O [MnSO4·H2O, Co（NO3）2·6H2O, ZnSO4·7H2O] and imidazole at pH≈7.5. The structure of Na9[{Na（H2O）2}3{Ni（C3H4N2）}3（SbW9O33）2]·32H2O was determined by single crystal X-ray diffraction. Polyanion [{Na（H2O）2}3{Ni（C3H4N2）}3（SbW9O33）2}3]^9- has approximate C3v symmetry, imidazole coordinated six-nuclear duster [{Na（H2O）2}3{Ni（C3H4N2）}3]^9＋ is encapsulated between two （α-SbW9O33）^9-, the three rings of imidazole in the polyanion are perpendicular to the horizontal plane formed by six metals （Na-Ni-Na-Ni-Na-Ni） in the central belt, and x-stacking interactions exist between imidazoles of neighboring polyanions with dihedral angel of 60%. The compounds were also characterized by IR, UV-Vis spectra, TG and DSC, and the thermal decomposition mechanism of the four compounds was suggested by TG curves.
The imidazole covalently coordinated sandwich-type heteropolymngstates Na9[ {Na（H=O2}3{M（C3H4N2）}3（ Sb W9O33）2]·xH=O（M=Ni^Ⅱ, Co^Ⅱ, Zn^Ⅱ, Mn^Ⅱ） were obtained by the reaction of Na2WO4·2H2O, SbCl3·6H2O, NiCl2·6H2O [MnSO4·H2O, Co（NO3）2·6H2O, ZnSO4·7H2O] and imidazole at pH≈7.5. The structure of Na9[{Na（H2O）2}3{Ni（C3H4N2）}3（SbW9O33）2]·32H2O was determined by single crystal X-ray diffraction. Polyanion [{Na（H2O）2}3{Ni（C3H4N2）}3（SbW9O33）2}3]^9- has approximate C3v symmetry, imidazole coordinated six-nuclear duster [{Na（H2O）2}3{Ni（C3H4N2）}3]^9＋ is encapsulated between two （α-SbW9O33）^9-, the three rings of imidazole in the polyanion are perpendicular to the horizontal plane formed by six metals （Na-Ni-Na-Ni-Na-Ni） in the central belt, and x-stacking interactions exist between imidazoles of neighboring polyanions with dihedral angel of 60%. The compounds were also characterized by IR, UV-Vis spectra, TG and DSC, and the thermal decomposition mechanism of the four compounds was suggested by TG curves.
基金
Project supported by the Natural Science Foundation of Shaanxi Province （No. 2003B01） and the Education Commission of Shaanxi Province （Nos. 03JK077, 03JS006）.