摘要
In situ A356/TiB2 composites were successfully fabricated via in-melt reaction among aluminium alloy, K2TiF6 and KBF4 compounds. The composite was examined by using XRD, SEM and EDX techniques. The experimental results reveal that TiB2 are dispersed homogeneously into the aluminium alloy matrix. The mechanical properties of the composites increase significantly with the addition of reinforcement, and the tensile fractography of the composite exhibits to be ductile though the elongation of the composites decreases compared with the unreinforced matrix alloy.
In situ A356/TiB2 composites were successfully fabricated via in-melt reaction among aluminium alloy, K2TiF6 and KBF4 compounds. The composite was examined by using XRD, SEM and EDX techniques. The experimental results reveal that TiB2 are dispersed homogeneously into the aluminium alloy matrix. The mechanical properties of the composites increase significantly with the addition of reinforcement, and the tensile fractography of the composite exhibits to be ductile though the elongation of the composites decreases compared with the unreinforced matrix alloy.
出处
《中国有色金属学会会刊:英文版》
CSCD
2006年第A03期1366-1369,共4页
Transactions of Nonferrous Metals Society of China
关键词
微观结构
钛合金
张力
机械性能
aluminium matrix composites
in situ
A356 alloy
TiB2
tensile properties