A kind of aluminum cooler was manufactured by means of vacuum brazing technique, and the cooler was examined by hydraulic pressure test. The result indicates that the test pressure of the cooler can reach 15 MPa.The fracture of the brazing joint belongs to the mixture type. There are secondary cracks, dimples, cleavage plane and grain-boundary features on the failure surface. The cracking process of aluminum cooler is as follows. The cracks are initiated on the interface, then expand under sub-critical state. When the stress on the remained zone reaches the maximum notch tensile strength of the brazing joint or the crack length reaches the critical value that the brazing joint fracture toughness property permits, the cooler will break sharply.
A kind of aluminum cooler was manufactured by means of vacuum brazing technique, and the cooler was examined by hydraulic pressure test. The result indicates that the test pressure of the cooler can reach 15 MPa. The fracture of the brazing joint belongs to the mixture type. There are secondary cracks, dimples, cleavage plane and grain-boundary features on the failure surface. The cracking process of aluminum cooler is as follows. The cracks are initiated on the interface, then expand under sub-critical state. When the stress on the remained zone reaches the maximum notch tensile strength of the brazing joint or the crack length reaches the critical value that the brazing joint fracture toughness property permits, the cooler will break sharply.
出处
《中国有色金属学会会刊：英文版》
CSCD
2006年第A03期1388-1391,共4页
Transactions of Nonferrous Metals Society of China