Tensile and fracture behavior of DZ951 Ni-base superalloy

Tensile and fracture behavior of DZ951 Ni-base superalloy
下载PDF
导出
摘要 The tensile and fracture behavior of DZ951 directionally solidified Ni-base superalloy was studied in the temperature range of 20-1 100℃. The fracture mode was examined by scanning electron microscopy. The results show the experimental temperature has no significant effect on the tensile strengths, which are greater than 1 000 MPa from room temperature to 800℃. The yield strength reaches its maximum (970 MPa) at 800℃. When the experimental temperature is higher than 800℃, the tensile and yield strengths decrease evidently and the ductility increases remarkably. The fractograph of fracture surface for the tensile specimen at room temperature shows a dimple-ductile fracture mode. The fractograph from 600 to 800℃shows a slide fracture mode. The fractograph from 900 to 1 100℃exhibits a creep rupture mode with uneven deformation. The tensile and fracture behavior of DZ951 directionally solidified Niobase superalloy was studied in the temperature range of 20-1 100 ℃. The fracture mode was examined by scanning electron microscopy. The results show the experimental temperature has no significant effect on the tensile strengths, which are greater than 1 000 MPa from room temperature to 800 ℃. The yield strength reaches its maximum (970 MPa) at 800 ℃. When the experimental temperature is higher than 800 ℃, the tensile and yield strengths decrease evidently and the ductility increases remarkably. The fractograph of fracture surface for the tensile specimen at room temperature shows a dimple-ductile fracture mode. The fractograph from 600 to 800 ℃ shows a slide fracture mode. The fractograph from 900 to 1 100 ℃ exhibits a creep rupture mode with uneven deformation.
出处 《中国有色金属学会会刊:英文版》 CSCD 2006年第A03期1949-1952,共4页 Transactions of Nonferrous Metals Society of China
关键词 高温合金 张力 固相 强度 Ni-base superalloy tensile strength yield strength fractograph
  • 相关文献

参考文献11

  • 1SIMS C T,STOLOFF N S,HAGREL W C.Superalloy Ⅱ[M].New York:Boston Rougeclaitor Publishing Company,1987:3-26.
  • 2MATTHEW J,DONACHIE J.Superalloy[M].Ohio:American Society for Metals,Metal Park,1984:3-14.
  • 3SCHEUNEMANN FRERKER G,GABRISCH H,FELLER KNIEPMEIER M.Dislocation microstructure in a single crystal Ni-base superalloy after tensile testing at 823 K in the[001] direction[J].Phil Mag A,1992,65(6):1353-1368.
  • 4SENGUPTA A,PUTATUNDA S K,BARTOSIEWICZ L,et al.Tensile behavior of a new single crystal Ni-base superalloy (CMSX-4) at room and elevated temperatures[J].J Mater Eng Perform,1994,3(5):664-672.
  • 5BETTGE D,OSTERLE W,ZIEBS J.Temperature dependence of yield strength and elongation of the Nickel-base superalloy IN738LC and the corresponding microstructural[J].Z Metallkd,1995,86(3):190-197.
  • 6FELLER-KNIEPMEIER M,LINK T,POSCHMANN L,et al.Temperature dependence of deformation mechanisms in a single crystal Ni-base alloy with high volume fraction of γ′ phase[J].Acta Mater,1996,44(6):2397-2407.
  • 7Institute of Metal Research,Chinese Academy of Sciences.Report of research and development of a directionally solidified Co-base superalloy DZ40M[R].1998.
  • 8NABARRO F R N,DUESERY M S.Dislocations in Solids[M].Amsterdam:North-Holland Publishing Company,1996:113-119.
  • 9COPLRY S M,KEAR B H.A dynamic theory of coherent precipitation hardening with application to nickel-base superalloys[J].Trans AIME,1967,239:984-992.
  • 10KEEP B H,WILSDORF H G F.Dislocation configurations in plastically deformed polycrystalline Cu3Au alloys[J].Trans AIME,1962,224:382-386.

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部