块体纳米晶Al-Zn-Mg-Cu合金的热处理 被引量：2

Heat treatment of bulk nanocrystalline Al-Zn-Mg-Cu alloy
下载PDF
导出
摘要 利用液氮球磨、真空热压和挤压工艺制备块体纳米晶Al-Zn-Mg-Cu合金，并对其固溶和时效处理进行研究，得到时效硬度曲线。利用X射线衍射仪和透射电镜对该合金热处理前后的微观组织进行分析，结果表明：块体制备过程中析出的MgZn2可以通过固溶处理使其回溶并在时效后沉淀析出；热压后晶粒尺寸为50～100nm，热处理后晶粒长大到100nm，部分晶粒达到200nm。 Bulk nanocrystalline Al-Zn-Mg-Cu alloy was fabricated by cryomilling combined with vacuum hot pressing and extrusion. The aging-curve was obtained. The crystal structures and microstructures before and after heat treatment were investigated by X-ray diffractometry （XRD） and transmission electron microscopy（TEM）, respectively. The results show that the deposition（MgZn2） of consolidation can be dissolved again by solid-solution, and precipitated during aging. The grain sizes of the bulk nanocrystalline Al-Zn-Mg-Cu alloy produced by vacuum hot pressing are 50-100 nm, some of them grow to 100 nm even part of them reach 200 nm after heat-treatment.
作者 陈汉宾 程军胜 杨滨 张济山 樊建中 田晓风
机构地区 北京科技大学新金属材料国家重点实验室 北京有色金属研究总院
出处 《中国有色金属学报》 EI CAS CSCD 北大核心 2007年第1期30-34,共5页 The Chinese Journal of Nonferrous Metals
基金 国家高技术研究发展计划资助项目(2002AA302502)
关键词 铝合金 块体纳米晶 低温球磨 固溶处理 时效处理 微观组织 aluminum alloy bulk nanocrystalline cryomilling solid-solution aging microstructure
分类号 TG156 [金属学及工艺—热处理]
  • 相关文献

参考文献18

  • 1Huang B,Perez R J,Lavernia E J.Grain growth of nanocrystalline Fe-Al alloys produced by cryomilling in liquid argon and nitrogen[J].Mater Sci Eng A,1998,A255:124-132.
  • 2Miller M K,Wirth B D,Odette G R.Precipitation in neutron-irradiated Fe-Cu and Fe-Cu-Mn model alloys:a comparison of APT and SANS data[J].Mater Sci Eng A,2003,A354:133-139.
  • 3Yin W M,Whang S H,Mirshams R A.Effect of interstitials on tensile strength and creep in nanostructured Ni[J].Acta Mater,2005,53:383-392.
  • 4Han B Q,Matejczyk D,Zhou F,et al.Mechanical behavior of a cryomilled nanostructured Al-7.5 pct Mg alloy[J].Metall Mater Trans A,2004,A35:947-949.
  • 5Park Y S,Chung K H,Kim N J,et al.Microstructural investigation of nanocrystalline bulk Al-Mg alloy fabricated by cryomilling and extrusion[J].Mater Sci Eng A,2004,A374:211-216.
  • 6Witkin D,Lee Z,Rodriguez R,Nutt S,et al.Al-Mg alloy engineered with bimodal grain size for high strength and increased ductility[J].Scripta Mater,2003,49:297-302.
  • 7Han B Q,Lee Z,Nutt S R,et al.Mechanical properties of an ultrafine-grained Al-7.5 Pct Mg alloy[J].Metall Mater Trans A,2003,A34:603-613.
  • 8Zheng L J,Chen C Q,Zhou T T,et al.Structure and properties of ultrafine-grained Al-Zn-Mg-Cu and Al-Cu-Mg-Mn alloys fabricated by ECA pressing combined with thermal treatment[J].Mater Character,2002,49:455-461.
  • 9Stolyarov V V,Latysh V V,Shundalov V A,et al.Influence of severe plastic deformation on aging effect of Al-Zn-Mg-Cu-Zr alloy[J].Mater Sci Eng A,1997,A234:339-342.
  • 10杨滨,程军胜,樊建中,田晓风,陈汉宾,张济山.低温球磨纳米晶Al-Zn-Mg-Cu合金组织的演变[J].金属学报,2005,41(11):1195-1198. 被引量：5

二级参考文献42

  • 1程军胜,杨滨,张济山,田晓风,樊建中.块体金属纳米材料成形技术研究进展[J].材料导报,2004,18(11):63-65. 被引量：3
  • 2卢柯,刘学东,张皓月,胡壮麒.纯镍纳米晶体的晶格膨胀[J].金属学报,1995,31(2). 被引量：17
  • 3Gleiter H.Nanocrystalline materials[J].Prog.Mater.Sci.,1989,33(4):223.
  • 4Perez R J,Huang B,Lavernia E J.Thermal stability of nanocrystalline Fe-10wt% Al produced by cryogenic mechanical alloying[J].Nanostruc.Mater.,1996,7(5):565.
  • 5Rawers J C,Harlow D G.Understanding the strength of hot-pressed nanostructured powder compacts[J].J.Mater.Eng.Perform,1999,8:35.
  • 6Zhou F,Witkin D,Nutt S R,et al.Formation of nanostructure in Al produced by a low-energy ball milling at cryogenic temperature[J].Mater.Sci.Eng.,2004,A375-377:917.
  • 7Choi J H,Moon K I,Kim J K,et al.Consolidation behavior of nanocrystalline Al-5at%Ti alloys synthesized by cryogenic milling[J].J.Alloy Compd.,2001,315:178.
  • 8Lu L,Sui M L,Lu K.Cold rolling of bulk nanocrystalline copper[J].Acta Mater.,2001,49:4127.
  • 9Sun X,Reglero R,Sun X,et al.Microhardness of bulk and higher density nanocrystalline copper obtained by hot compaction[J].Mater.Chem.Phys.,2000,63:82.
  • 10Zhang X,Wang H,Kassem M,et al.Preparation of bulk ultrafine-grained and nanostructured Zn,Al and their alloys by in situ consolidation of powders during mechanical attrition[J].Scripta Mater.,2002,46:661.

共引文献47

同被引文献32

  • 1厉沙沙,李炯利,李伟,熊艳才.低温球磨制备纳米晶7050合金粉体[J].稀有金属材料与工程,2012,41(S2):761-764. 被引量：2
  • 2王洪斌,黄进峰,崔华,张永安,熊柏青,张济山.喷射成形Al-Zn-Mg-Cu合金的显微组织演变[J].金属学报,2004,40(8):827-832. 被引量：12
  • 3徐崇义,李念奎.2×××系铝合金强韧化的研究与发展[J].轻合金加工技术,2005,33(8):13-17. 被引量：39
  • 4杨滨,程军胜,樊建中,田晓风,陈汉宾,张济山.低温球磨纳米晶Al-Zn-Mg-Cu合金组织的演变[J].金属学报,2005,41(11):1195-1198. 被引量：5
  • 5陈汉宾,程军胜,杨滨,张济山,樊建中,田晓风.放电等离子烧结制备Al-Zn-Mg-Cu纳米晶合金的组织[J].北京科技大学学报,2007,29(3):293-297. 被引量：4
  • 6D.B.Witkin, E.J.Lavernia, Synthesis and mechanical behavior of nanostructured materials via cryomilling, Progress in Materials Science, 51, 1(2006).
  • 7Y.S.Park, K.H.Chung, N.J.Kim, E.J.Lavernia, Mierostructural investigation of nanocrystalline bulk Al-Mg alloy fabricated by cryomilling and extrusion, Materials Science and Engineering A, 374, 211(2004).
  • 8B.Q.Han, E.J.Lavernia, F.A.Mohamed, Tension and compression behaviors of bulk ultrafine-grained Al-7.5wt%Mg alloy, Philosophical Magazine Letters, 83(2), 89(2003).
  • 9B.Q.Han, Z.Lee, D.B.Witkin, S.Nutt, E.J.Lavernia, Deformation behavior of bimodal nanostructured 5083 Al alloys, Metallurgical and Materials Transactions A, 36(4), 957(2005).
  • 10J.C.Ye, L.Ajdelazztajn, J.M.Schoenung, Bulk nanocrystalline aluminum 5083 alloy fabricated by a novel technique, cryomilling and spark plasma sintering, Meatallurgical and Materials Transactions A, 37(8), 2569(2006).

引证文献2

二级引证文献4

中国有色金属学报
2007年 第1期

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部