以四氯化钛为原料,采用液相法制备出粒径约为12 nm,比表面积为229.77 m2/g的纳米二氧化钛粉体。并通过实验,用XRD、SEM对粒子的形貌、晶型、粒径进行了表征对比,并结合二氧化钛粉体制备的产率,对主要工艺参数进行了分析与讨论。
The titanium dioxide powder with is prepared using liquid phase methods with diameter of 12 nm and specific surface area of 229.77 m2/g TiC14 as starting material. The morphology, crystal shape and size of TiO2 nano - powder is characterized by XRD and SEM. The main processing parameters are analyzed and discussed considering the yield of titanium dioxide powder.