EFFECTS OF TREATMENT TIME ON CORROSION OF DIFFUSION-ALLOYED COATINGS OF PURE MAGNESIUM 被引量:2

EFFECTS OF TREATMENT TIME ON CORROSION OF DIFFUSION-ALLOYED COATINGS OF PURE MAGNESIUM
下载PDF
导出
摘要 The corrosion resistance of pure magnesium with surface alloying layer obtained by a solid diffusion alloying technique has been analyzed. To establish the optimum treatment time, the experiments were performed at 480℃ for different solid diffusion time (8, 16, and 24h). The diffusion interaction effectiveness between Zn, Al mix powder and the sample surface, depending on the treatment time for diffusion at given temperatures, has an obvious influence on corrosion resistance and corrosion mechanism. Corrosion properties were studied using the constant immersion test (in 3.0% NaCl solution, temperature is (28±1)℃, and time is 96h). Optical microscopy (OM) and EDS (energy dispersive spectrum) composition analysis were used to examine the cross-sectional microstructural characteristics of alloyed layer of treated samples. It is shown that in comparison with the untreated samples, the treated ones possess a better corrosion resistance. The Al5Mg11Zn4 phase, which formed as a continuous phase due to the diffusion of Al, Zn, and Mg elements and subsequent interaction on the outermost layer of diffusion alloying zones (especially the samples treated for 24h at 480℃), was inert to the chloride solution compared with pure magnesium and acted as a corrosion barrier, and therefore the best corrosion resistance was obtained. This protective action of Al5Mg11Zn4 phase was found to change with its amount, which was controlled by the diffusion time at given temperature. It was concluded that the continuous Al5Mg11Zn4 phase (WP-zone) of the reacted layer in pure magnesium was beneficial from the point of view of corrosion resistance. The corrosion resistance of pure magnesium with surface alloying layer obtained by a solid diffusion alloying technique has been analyzed. To establish the optimum treatment time, the experiments were performed at 480℃ for different solid diffusion time (8, 16, and 24h). The diffusion interaction effectiveness between Zn, Al mix powder and the sample surface, depending on the treatment time for diffusion at given temperatures, has an obvious influence on corrosion resistance and corrosion mechanism. Corrosion properties were studied using the constant immersion test (in 3.0% NaCl solution, temperature is (28±1)℃, and time is 96h). Optical microscopy (OM) and EDS (energy dispersive spectrum) composition analysis were used to examine the cross-sectional microstructural characteristics of alloyed layer of treated samples. It is shown that in comparison with the untreated samples, the treated ones possess a better corrosion resistance. The Al5Mg11Zn4 phase, which formed as a continuous phase due to the diffusion of Al, Zn, and Mg elements and subsequent interaction on the outermost layer of diffusion alloying zones (especially the samples treated for 24h at 480℃), was inert to the chloride solution compared with pure magnesium and acted as a corrosion barrier, and therefore the best corrosion resistance was obtained. This protective action of Al5Mg11Zn4 phase was found to change with its amount, which was controlled by the diffusion time at given temperature. It was concluded that the continuous Al5Mg11Zn4 phase (WP-zone) of the reacted layer in pure magnesium was beneficial from the point of view of corrosion resistance.
出处 《Acta Metallurgica Sinica(English Letters)》 SCIE EI CAS CSCD 2007年第1期72-78,共7页 金属学报(英文版)
基金 supported by Shaan Xi Provincial Natural Science Foundation of China(No.2004E111).
关键词 pure magnesium solid diffusion treatment time MICROSTRUCTURE CORROSION pure magnesium solid diffusion treatment time microstructure corrosion
  • 相关文献

参考文献11

  • 1I. Shigematsu,M. Nakamura,N. Saitou,K. Shimojima.Surface treatment of AZ91D magnesium alloy by aluminum diffusion coating[J].Journal of Materials Science Letters.2000(6)
  • 2B.M azurkiew icz. Corrosion Science . 1983
  • 3Y .Y .Li,W .W .Zhang,Y .Liu,W .P.Chen,and D .H .N i. Special Casting & Nonferrouy Alloys . 2004
  • 4R.C.Zeng,W .K e,Y .B.X u,E.H .H an,and Z.Y .Zhu. Acta Metallurgica . 2001
  • 5H .Inoue,K .Sugahara,A .Y am am oto,and H .Tsubakino. Corrosion Science . 2002
  • 6K .Z.Chong,T.S.Shih. Journal of Materials Chemistry . 2003
  • 7H .K uw ahara,Y .A bdullat,and M .O hta. Materials Science Forum . 2000
  • 8E.Zhang,L.P.X u,and K .Y ang. Scripta Materialia . 2005
  • 9G .L.Song,A .A trens,and M .D argusch. Corrosion Science . 1999
  • 10R.A m bat,N .N .A ung,and W .Zhou. Corrosion Science . 2000

同被引文献17

引证文献2

二级引证文献6

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部