Barium strontium titanate/magnesia （BSTO/MgO） ferroelectric material for phase shift was prepared by traditional solid phase synthesis. The phase distribution, microstructure and electric properties were investigated. The results show that no secondary phase appears in the composites and the dimension of grains distributes uniformly. With 50 wt% MgO content, the dielectric tunability reaches 17.5 % in the external DC field of 4 000 Vomm^-1 and the microwave loss at about 2.5 GHz is 8×10^-3. Hence, it can be applied in tunable microwave phase shifters.
Barium strontium titanate/magnesia （BSTO/MgO） ferroelectric material for phase shift was prepared by traditional solid phase synthesis. The phase distribution, microstructure and electric properties were investigated. The results show that no secondary phase appears in the composites and the dimension of grains distributes uniformly. With 50 wt% MgO content, the dielectric tunability reaches 17.5 % in the external DC field of 4 000 Vomm^-1 and the microwave loss at about 2.5 GHz is 8×10^-3. Hence, it can be applied in tunable microwave phase shifters.
基金
Funded by the Commission of Science Technology and Industry for National Defense(No.MKPT-03-155)