An annealed TC4 titanium alloy sheet was treated by high density electropulsing(Jmax=(5.09-5.26)×103A/mm2,tp=110μs)under ambient conditions.The effect of electropulsing treatment(EPT)on the plastic deformation behavior of TC4 titanium alloysheet was studied using uniaxial tension tests.The experimental results indicate that electropulsing treatment significantly changesthe mechanical properties of sheet metal:the uniform elongation is increased by 35%,the yield stress is decreased by 19.8%and theyield to tensile ratio is decreased by 17.6%.It is of significant meaning to improve the formability of TC4 titanium alloy sheet.Theoptical microscope and scanning electron microscope(SEM)were used to examine the changes of the microstructure and the fracturemorphology before and after the electropulsing treatment.It is found that recrystallization occurs in the sheet metal and dimples infracture surface are large and deep after the electropulsing treatment.The research results show that the electropulsing treatment is aneffective method to improve the formability of titanium alloy sheets.
An annealed TC4 titanium alloy sheet was treated by high density electropulsing （Jmax=（5.09-5.26）×10^3A/mm^2, tp： 110 μs） under ambient conditions. The effect of electropulsing treatment（EPT） on the plastic deformation behavior of TC4 titanium alloy sheet was studied using uniaxial tension tests. The experimental results indicate that electropulsing treatment significantly changes the mechanical properties of sheet metal： the uniform elongation is increased by 35%, the yield stress is decreased by 19.8% and the yield to tensile ratio is decreased by 17.6%. It is of significant meaning to improve the formability of TC4 titanium alloy sheet. The optical microscope and scanning electron microscope（SEM） were used to examine the changes of the microstructure and the fracture morphology before and after the electropulsing treatment. It is found that recrystallization occurs in the sheet metal and dimples in fracture surface are large and deep after the electropulsing treatment. The research results show that the electropulsing treatment is an effective method to improve the formability of titanium alloy sheets.
出处
《中国有色金属学会会刊：英文版》
EI
CSCD
2007年第1期87-92,共6页
Transactions of Nonferrous Metals Society of China
关键词
钛合金
电脉冲技术
机械性能
扫描电镜
TC4 alloy
titanium alloy sheet
electropulsing treatment
formability