摘要
Thin films of titanium carbide and amorphous hydrogenated carbon have been synthesized on titanium aluminium alloy substrates by PSII assisted MW-ECRCVD with a mirror field. The microstructure, chemical composition and mechanical property were investigated. Using XPS and TEM, the films were identified to be a-C：H film containing TiC nanometre grains （namely, the so-called nanocomposite structure）. The size of TiC grains of nanocomposite TiC/DLC film is about 5 nm. The nanocomposite structure has obvious improvement in the mechanical properties of DLC film. The hardness of a-C：H film with Ti is enhanced to 34 G Pa~ while that of a-C：H film without Ti is about 12 G Pa, and the coherent strength is also obviously enhanced at the critical load of about 35N.
Thin films of titanium carbide and amorphous hydrogenated carbon have been synthesized on titanium aluminium alloy substrates by PSII assisted MW-ECRCVD with a mirror field. The microstructure, chemical composition and mechanical property were investigated. Using XPS and TEM, the films were identified to be a-C：H film containing TiC nanometre grains （namely, the so-called nanocomposite structure）. The size of TiC grains of nanocomposite TiC/DLC film is about 5 nm. The nanocomposite structure has obvious improvement in the mechanical properties of DLC film. The hardness of a-C：H film with Ti is enhanced to 34 G Pa~ while that of a-C：H film without Ti is about 12 G Pa, and the coherent strength is also obviously enhanced at the critical load of about 35N.