The two kinds of super absorbent resins from carboxymethyl cellulose were synthesized with the potassium persulphate and methylenebisacrylamide as initiator and cross linker respectively by radical polymerization in aqueous solution. Thestructures of the two resins were characterized with Fourier transform infrared spectroscopy FTIR, scanning electron miscroscopy （SEM）, and environment scanning electron miscroscopy （ESEM）, the results indicate that the fibriform of the carboxymethyl cellulose （CMC） is disappeared and the crusslink networks in eopolymer of carboxymethyl cellulose-graft-polyacrylic acid（CMC-g-PAA） are denser than that of eopolymer of carboxymethyl cellulose-graft-poly （acrylic acid-co-N-vinyl Pyrrolidone） （CMC-g- PAA-co-PVP）. The comparison between the two resins in absorption capacities is that CMC-g-PAA is better in the water-keep capability being heated, while CMC-g-PAA-co-PVP is better in the water absorbency and salt resistance.
The two kinds of super absorbent resins from carboxymethyl cellulose were synthesized with the potassium persulphate and methylenebisacrylamide as initiator and cross linker respectively by radical polymerization in aqueous solution. Thestructures of the two resins were characterized with Fourier transform infrared spectroscopy FTIR, scanning electron miscroscopy （SEM）, and environment scanning electron miscroscopy （ESEM）, the results indicate that the fibriform of the carboxymethyl cellulose （CMC） is disappeared and the crusslink networks in eopolymer of carboxymethyl cellulose-graft-polyacrylic acid（CMC-g-PAA） are denser than that of eopolymer of carboxymethyl cellulose-graft-poly （acrylic acid-co-N-vinyl Pyrrolidone） （CMC-g- PAA-co-PVP）. The comparison between the two resins in absorption capacities is that CMC-g-PAA is better in the water-keep capability being heated, while CMC-g-PAA-co-PVP is better in the water absorbency and salt resistance.
基金
Basic Research Foundation of Beijing Institute of Technology (BIT-UBF-200504E4202)