The microstructures, the phase transformation characteristics, and the mechanical properties of the Ti50Ni47Fe3 alloy in as-forged and as-cross-rolled states were investigated. It is found that, after cross-rolling, the phase transformation temperature （Ms） of the alloy decreases drastically and the grains get refined. Moreover, its yield strength and fracture strength after cross-rolling hit 540 MPa and 687 MPa respectively, up by about 200 MPa over those in as-forged state.
The microstructures, the phase transformation characteristics, and the mechanical properties of the Ti50Ni47Fe3 alloy in as-forged and as-cross-rolled states were investigated. It is found that, after cross-rolling, the phase transformation temperature （Ms） of the alloy decreases drastically and the grains get refined. Moreover, its yield strength and fracture strength after cross-rolling hit 540 MPa and 687 MPa respectively, up by about 200 MPa over those in as-forged state.