Scandia and rhenium doped tungsten powders were prepared by solid-liquid doping combined with two-step reduction method. The particle size of doped tungsten and distribution of scandia and rhenium were studied by SEM, EDS, XRD and granularity analysis. Experimental results showed that scandia distributed evenly on the surface of tungsten particles. Addition of scandia and rhenium decreased the particle size of doped tungsten, and the more the content of scandia and rhenium, the smaller the doped tungsten particles. Tungsten powders doped with 3 % Sc2O3 and 3 % Re （mass fraction） had an average size of about 80 nm in diameter. The mechanism of the decrease in the tungsten particle size was discussed.
Scandia and rhenium doped tungsten powders were prepared by solid-liquid doping combined with two-step reduction method. The particle size of doped tungsten and distribution of scandia and rhenium were studied by SEM, EDS, XRD and granularity analysis. Experimental results showed that scandia distributed evenly on the surface of tungsten particles. Addition of scandia and rhenium decreased the particle size of doped tungsten, and the more the content of scandia and rhenium, the smaller the doped tungsten particles. Tungsten powders doped with 3 % Sc2O3 and 3 % Re （mass fraction） had an average size of about 80 nm in diameter. The mechanism of the decrease in the tungsten particle size was discussed.
基金
Project supported by the National Natural Science Foundation of China (50571001)
the National "863"Project(2006AA03Z524)