摘要
以TiO2高炉渣为基料配制的合成渣对钢液脱氮的效果进行了实验室试验研究，结果表明：在Ar气保护下，对低碳铝脱氧钢液脱氮，其脱氮率达60％以上，最低［N］含量约10×10-6。
The removal of nitrogen from liquid steel by TiO2 based blast furnace slag was investigated in laboratory. The testing results show that more than 60 percent of nitrogen was removed from low carbon alu minium-killed steel with shielded argon atmosphere and the lowest [N] content about 10×10-6 was obtained.
出处
《特殊钢》
北大核心
1997年第2期9-13,共5页
Special Steel
关键词
钢液
合成渣
脱氮
炼钢
Liquid Steel, Fluxes. Removal of Nitrogen