摘要
This paper studied the appearance transition of microdischarges, the phase composition and the morphology evolution of the oxide film formed by microarc oxidation on AZ91D magnesium alloy. The appearance of microdischarges population experienced apparent changes in size, spatial density and color, which was related with the changes of the type and quantity of the disintegrated gas bubbles generated at the interface between the electrolyte and substrate. Correspondingly, the diameter of micropores together with net-like fine microcracks increased when a higher voltage was employed. The coating was composed of MgO, MgAl2O4 and there existed a fluoride-enriched zone of about 3-5μm at the film/substrate interface.
This paper studied the appearance transition of microdischarges, the phase composition and the morphology evolution of the oxide film formed by microarc oxidation on AZ91D magnesium alloy. The appearance of microdischarges population experienced apparent changes in size, spatial density and color, which was related with the changes of the type and quantity of the disintegrated gas bubbles generated at the interface between the electrolyte and substrate. Correspondingly, the diameter of micropores together with net-like fine microcracks increased when a higher voltage was employed. The coating was composed of MgO, MgAl2O4 and there existed a fluoride-enriched zone of about 3-5μm at the film/substrate interface.
基金
the Natural Science Foundation of Hubei Province (2002ABB051)