摘要
The effects of Pb content on crystallographic phase, microstructure, electric-properties of PMSZT piezoelectric ceramics were studied. The crystallographic phase and microstructure of the ceramics were examined by using X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The experimental result shows that the samples consist of a mixture of tetragonal and rhombohedral phases in the range of lead contents x=0.95-1.06, grains grow up homogeneously and the minimum value of Curie temperature was obtained with x-=1.02. With Pb content x〈l.02 or x〉1.02, the Curie temperature moves towards a high temperature. A well-situated electric-properties of ET33/E0 （1660）, d33 （344pC/N）, Kp （0.684）, Qm （2350）,tan 3（0.0030） were obtained when lead content x=1.02.
The effects of Pb content on crystallographic phase, microstructure, electric-properties of PMSZT piezoelectric ceramics were studied. The crystallographic phase and microstructure of the ceramics were examined by using X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The experimental result shows that the samples consist of a mixture of tetragonal and rhombohedral phases in the range of lead contents x=0.95-1.06, grains grow up homogeneously and the minimum value of Curie temperature was obtained with x-=1.02. With Pb content x〈l.02 or x〉1.02, the Curie temperature moves towards a high temperature. A well-situated electric-properties of ET33/E0 （1660）, d33 （344pC/N）, Kp （0.684）, Qm （2350）,tan 3（0.0030） were obtained when lead content x=1.02.
基金
the National Natural Science Foundation of China (No.10232030)
Key Laboratory for Advanced Ceramics and Machining Technology of Ministry of Education(No.x06050)