摘要
研究了固溶温度对00Cr22Ni5Mo3N钢相比例及耐点蚀性能的影响。结果表明，在1000～1300℃，随着固溶温度的提高，00Cr22Ni5Mo3N钢组织中的铁素体含量逐渐增加，钢的耐点蚀性能呈曲线变化.本试验条件下，在1000～1150℃固溶处理时，该钢具有较好的耐点蚀性能，这与其化学成分、相析出、相比例及化学元素在两相中的分配比有直接的关系。
Effect of solution temperature on microstructure and pitting corrosion-resistant property of 00Cr22Ni5Mo3N has been studied. The results show that ferrite content increases and the pitting corrosion-resistant property presents a curve change along with the solution temperature elevation at 900-1 300℃. And good pitting corrosion-resistant property can be gained at the solution temperature of 1 000-1 150 ℃ , which has relation to chemical composition, phases precipitated, α/γ phase ratio and the distribution of elements in phases.
出处
《钢铁研究学报》
CAS
CSCD
北大核心
2007年第6期69-71,98,共4页
Journal of Iron and Steel Research