摘要
在水热法制备PLZT陶瓷中,运用正交试验方法,得到最佳的水热制备条件。采用XRD、TEM对粉体进行表征,结果表明,PLZT(4/53/47)陶瓷为纯四方相结构,平均粒径大小为80nm。
Through hydrothermal synthesis of the PLZT by orthogonal test,we obtained optimal preparation condition.The nanosized powders were analyzed by XRD and TEM,and the results show that PLZT nonapowders with tetragonal-phase in size of 80 nm are obtained.