Study was made on the effect of surface modification on the behaviors of cerium oxide nanopowders.A surfactant-sodium dodecyl sulfate（C12H25SO4Na）was used to modify the surface of CeO2 powder particles.The unmodified and modified CeO2 powders were characterized by using a powder comprehensive characteristic tester,laser particle size analyzer,specific surface area tester,X-ray diffraction tester,and a scanning electron microscope.The testing and analysis results showed that C12H25SO4Na surface modification might increase the flowability and dispersity,and decrease the specific surface area and agglomeration of CeO2 powders.The mechanism of the surface modification of CeO2 powder particles was also discussed.
Study was made on the effect of surface modification on the behaviors of cerium oxide nanopowders.A surfactant-sodium dodecyl sulfate（C12H25SO4Na）was used to modify the surface of CeO2 powder particles.The unmodified and modified CeO2 powders were characterized by using a powder comprehensive characteristic tester,laser particle size analyzer,specific surface area tester,X-ray diffraction tester,and a scanning electron microscope.The testing and analysis results showed that C12H25SO4Na surface modification might increase the flowability and dispersity,and decrease the specific surface area and agglomeration of CeO2 powders.The mechanism of the surface modification of CeO2 powder particles was also discussed.
基金
Project supported by the National Key Basic Research Program(NKBRP20047CCA03900)
National Natural Science Foundation of China(2056601)