摘要
介绍了常顶空冷器的腐蚀情况并且分析了腐蚀原因及防护措施。采用了钛保套后,延长空冷器的使用寿命达1倍以上。
The corrosion and corrosion causes of overhead air cooler of atmospheric distillation tower and protection measures were described. After application of titanium casing ,the service life of the cooler was two times that of the original.