Nanocrystals of KMgF3 single-doped and codoped with Ce^3＋ or/and Yb^3＋ were synthesized separately by the mi-croemulsion method. The X-ray diffraction（XRD） patterns were indexed to show that the KMgF3 crystal system was unchanged. The fluorescent spectra of KMgF3： Ce, Yb polycrystal powders were studied and compared with those of the Ce,Yb doped KMgF3 crystals produced using the high-temperature solid phase method. The diffuse reflection spectra and infrared emission of KMgF3： Ce, Yb were investigated. From the results, the authors could confirm that there were charge transfer processes from Ce^3＋ to Yb^3＋ in both KMgF3： Ce,Yb nanocrystals and polycrystal powders.
Nanocrystals of KMgF3 single-doped and codoped with Ce^3＋ or/and Yb^3＋ were synthesized separately by the mi-croemulsion method. The X-ray diffraction（XRD） patterns were indexed to show that the KMgF3 crystal system was unchanged. The fluorescent spectra of KMgF3： Ce, Yb polycrystal powders were studied and compared with those of the Ce,Yb doped KMgF3 crystals produced using the high-temperature solid phase method. The diffuse reflection spectra and infrared emission of KMgF3： Ce, Yb were investigated. From the results, the authors could confirm that there were charge transfer processes from Ce^3＋ to Yb^3＋ in both KMgF3： Ce,Yb nanocrystals and polycrystal powders.
基金
Supported by the Science Foundation of Changchun City of China(No.2005093)
the Science and Technology Departmentof Jilin Province,P.R.China(No.20050507).