摘要
Highly ordered cubic Zr-doped mesoporous silica was directly prepared with Evaporation-Induced Self Assembly method(EISA) with triblock copolymers(Pluronic P123) as the structure-directing agents.The mesoporous material was characterized via small-angle powder X-ray diffraction(XRD),transmission electron microscopy(TEM),and nitrogen adsorption.The results show that the product has a face-centered cubic structure with space group of Fd3m.N2 sorption revealed that the Zr-doped mesoporous silica has not only ordered structures,but also high surface area(550 m2/g),large pore volume(0.66 cm3/g),as well as uniform pore size(4.0 nm).
Highly ordered cubic Zr-doped mesoporous silica was directly prepared with Evaporation-Induced Self Assembly method(EISA) with triblock copolymers(Pluronic P123 ) as the structure-directing agents. The mesoporous material was characterized via small-angle powder X-ray diffraction (XRD) , transmission electron microscopy(TEM ), and nitrogen adsorption. The results show that the product has a face-centered cubic structure with space group of Fd3m. N2 sorption revealed that the Zr-doped mesoporous silica has not only ordered structures, but also high surface area(550 m^2/g) , large pore volume(0.66 cm^3/g) , as well as uniform pore size (4.0 nm).
出处
《高等学校化学学报》
SCIE
EI
CAS
CSCD
北大核心
2007年第8期1428-1430,共3页
Chemical Journal of Chinese Universities
基金
国家自然科学基金(批准号:20273026)资助
关键词
介孔二氧化硅
氧化锆
立方相
溶剂挥发法
Mesoporous silica
Zirconia
Cubic phase
Evaporation-induced self-assembly(EISA)