Nano-sized Fe3O4 powder was prepared through an Oxygenation-Hydrothermal method. The chitosan magnetic complex was prepared by coating chitosan on the surface of Fe3O4 powders through Microlatex-Crosslinking Method. The product was characterized by IR,XRD,TEM,Vibrating Sample Magnetometer (VSM),TG methods. Results show that the as-prepared powder is 25 nm in size and shows supermagnetism. The content of magnetite in microspheres is 37.8%. The mechanism for the coating reaction of chitosan to Fe3O4 nanoparticles is also suggested.
Nano-sized Fe3O4 powder was prepared through an Oxygenation-Hydrothermal method. The chitosan magnetic complex was prepared by coating chitosan on the surface of Fe3O4 powders through Microlatex-Crosslinking Method. The product was characterized by IR,XRD,TEM,Vibrating Sample Magnetometer （VSM）,TG methods. Results show that the as-prepared powder is 25 nm in size and shows supermagnetism. The content of magnetite in microspheres is 37.8%. The mechanism for the coating reaction of chitosan to Fe3O4 nanoparticles is also suggested.
出处
《无机化学学报》
SCIE
CAS
CSCD
北大核心
2007年第8期1491-1495,共5页
Chinese Journal of Inorganic Chemistry
基金
国家自然科学基金项目(No.20376085)
2005年中南大学大学生创新教育项目(No.lz0502)。