摘要
On the basis of the effect of carbon precipitation on the microstructure and properties of steel products below At temperature, a new thermal treatment method （temper-rapid cooling process） was studied. By the temper-rapid cooling process, the yield strengths of the high strength low carbon （HSLC） steel ZJ330 and SPA-H produced using the compact strip production （CSP） process increased from 340 to about 410 MPa and from 410 to about 450 MPa, respectively. The results indirectly indicated that there existed nanoscaled iron-carbon precipitates that have obvious precipitation effect on low carbon steel produced by CSP. The prospect of application is discussed.
On the basis of the effect of carbon precipitation on the microstructure and properties of steel products below At temperature, a new thermal treatment method （temper-rapid cooling process） was studied. By the temper-rapid cooling process, the yield strengths of the high strength low carbon （HSLC） steel ZJ330 and SPA-H produced using the compact strip production （CSP） process increased from 340 to about 410 MPa and from 410 to about 450 MPa, respectively. The results indirectly indicated that there existed nanoscaled iron-carbon precipitates that have obvious precipitation effect on low carbon steel produced by CSP. The prospect of application is discussed.
基金
the National Natural Science Foundation of China (No.50334010).