摘要
The glass-transition behavior of Pd40Cu30Ni10P20 bulk metallic glass was investigated by differential scanning calorimetry （DSC） and X-ray powder diffraction （XRD）. The effect of pressure on the crystallization behavior of Pd40Cu30Ni10P20 bulk glass was studied by in situ high-pressure and high-temperature X-ray powder diffraction using synchrotron radiation. Phase analyses show at least six crystalline phases in the crystallized sample, namely, monoclinic, tetragonal CuaPd-like, rhombohedral, fcc-Ni2Pd2P, fcc-（Ni, Pd） solid solution, and body-centered tetragonal （bct） NiaP-like phases. The onset crystallization temperature increases with pressure having a slope of 1 1 K/GPa in the range of 0 to 4 GPa. The results are attributed to the competing process between the thermodynamic potential barrier and the diffusion activation energy under pressure.
The glass-transition behavior of Pd40Cu30Ni10P20 bulk metallic glass was investigated by differential scanning calorimetry （DSC） and X-ray powder diffraction （XRD）. The effect of pressure on the crystallization behavior of Pd40Cu30Ni10P20 bulk glass was studied by in situ high-pressure and high-temperature X-ray powder diffraction using synchrotron radiation. Phase analyses show at least six crystalline phases in the crystallized sample, namely, monoclinic, tetragonal CuaPd-like, rhombohedral, fcc-Ni2Pd2P, fcc-（Ni, Pd） solid solution, and body-centered tetragonal （bct） NiaP-like phases. The onset crystallization temperature increases with pressure having a slope of 1 1 K/GPa in the range of 0 to 4 GPa. The results are attributed to the competing process between the thermodynamic potential barrier and the diffusion activation energy under pressure.
基金
the National Natural Science Foundation of Beijing (No.2042014).