The effect of cooling rate and Al content (A1≥30%) on the microstructure and hardness of Zn-based alloy was investigated by a wedge-formed sampl, The results show that the secondary dendrite arm space decreases decreases with the increase of the cooling rate. The hardness of the alloy is mainly correlatire with Al content and it further increases with the increase of Al content.