通过调节脉冲电流峰值电压,研究了脉冲电流峰值电压对AZ91镁合金凝固组织和力学性能的影响,并与MgCO3变质处理进行了对比。结果表明,随着脉冲电流峰值电压的增大,合金的凝固组织愈加细化,力学性能不断提高;当脉冲电流峰值电压达到2000V时,脉冲电流处理试样的抗拉强度比未处理试样提高了25%、伸长率提高了128%,比变质处理的抗拉强度提高了4%、伸长率提高了14%。
The effects of different pulsed electric current peak values on solidification structure and mechanical properties of AZ91magnesium alloy have been investigated, which was compared with that of the alloy treated by MgCO3. The results show that with increasing the peak voltage of pulsed current, the solidification structure of the magnesium alloy can be greatly refined and the mechanical properties can be improved. With the peak voltage of 2000V, compared with the un-treated sample and with modified samples, the pulsed current treated samples can be increased by 25% and by 4% in tensile strength, and by 128% and by 14% in elongation, respectively.
出处
《特种铸造及有色合金》
CAS
CSCD
北大核心
2007年第8期633-635,共3页
Special Casting & Nonferrous Alloys
关键词
脉冲电流
AZ91镁合金
凝固组织
力学性能
Pulsed Current, AZ91 Magnesium Alloy, Solidification Structure, Mechanical Properties