摘要
Thin films of ZnO were electrodeposited from an aqueous solution of Zn(NO3)2 on indium tin oxide(ITO)-covered glass substrate. The analysis of X-ray diffraction(XRD) and scanning electron micrograph(SEM) indicated that the obtained ZnO films had a compact hexagonal wurtzite type structure with preferable (002) growth direction. A sharp near-UV emission peak located au 380 nm and a strong orange-red emission peak located at 593 nm were observed in the photoluminescence, when excited with 325 nm wavelength at room temperature. Then the prepared ZnO films were introduced as anode phosphors into the field emission test. It was found that orange-red cathode-luminescence was observed and the luminescent brightness was enhanced by annealing. When annealing temperature increased about 600 ℃, the photoluminescence with peak of 531 nm and the green cathode-luminescence were observed. The tests showed that the brightness of about 2×102 cd/m2 was obtained at electric field of 2 V/μm for annealed sample. The results revealed that the film could be a good kind of low-voltage drived cathode-luminescence phosphor.
Thin films of ZnO were electrodeposited from an aqueous solution of Zn(NO3 )2 on indium tin oxide(ITO)-covered glass substrate. The analysis of X-ray diffraction(XRD) and scanning electron micrograph (SEM) indicated that the obtained ZnO films had a compact hexagonal wurtzite type structure with preferable (002) growth direction. A sharp near-UV emission peak located at 380 nm and a strong orange-red emission peak located at 593 nm were observed in the photoluminescence, when excited with 325 nm wavelength at room temperature. Then the prepared ZnO films were introduced as anode phosphors into the field emission test. It was found that orange-red cathode-luminescence was observed and the luminescent brightness was enhanced by annealing. When annealing temperature increased about 600 ℃, the photoluminescence with peak of 531 nm and the green cathode-luminescence were observed. The tests showed that the brightness of about 2 × 102 cd/m^2 was obtained at electric field of 2 V/μm for annealed sample. The results revealed that the film could be a good kind of low-voltage drived cathode-luminescence phosphor.
基金
Science and Technology Foundation of Education Ministry of China(205091)
关键词
电极淀积
氧化锌薄膜
光激发光
凝聚态
electrodeposition
ZnO thin films
photoluminescence
cathode-luminescence
field emission
phosphor