摘要
The hot-press temperature curves were researched and effects of hot-pressing temperature,thickness of veneer and the numbers of layer on mechanical properties of laminated veneer lumber(LVL)were analyzed with emphasis in the paper.Results showed that there was positive relationship between hot-pressing temperature and modulus of elastic(MOE);the modulus of rupture(MOR)of LVL was best when manufactured at 160 ℃.When the thickness of veneers was 3.25 mm the LVL usually destroyed due to veneer tearing;while when the thickness of veneers was 1.70 mm it easily splited in adhesive layer;the mechanical properties of LVL were best when the thickness of veneers was 1.70 mm;the 3 multinomial degrees of fitting the numbers of layers with MOE and MOR of Eucalyptus LVL matched very well,the R2 value were 0.951 6 and 0.981 2,respectively.
The hot-press temperature curves were researched and effects of hot-pressing temperature,thickness of veneer and the numbers of layer on mechanical properties of laminated veneer lumber(LVL)were analyzed with emphasis in the paper.Results showed that there was positive relationship between hot-pressing temperature and modulus of elastic(MOE);the modulus of rupture(MOR)of LVL was best when manufactured at 160 ℃.When the thickness of veneers was 3.25 mm the LVL usually destroyed due to veneer tearing;while when the thickness of veneers was 1.70 mm it easily splited in adhesive layer;the mechanical properties of LVL were best when the thickness of veneers was 1.70 mm;the 3 multinomial degrees of fitting the numbers of layers with MOE and MOR of Eucalyptus LVL matched very well,the R^2 value were 0.951 6 and 0.981 2,respectively.
出处
《林业科学》
EI
CAS
CSCD
北大核心
2007年第8期154-158,共5页
Scientia Silvae Sinicae
基金
国家林业局"948"项目"桉树人工林木材材性与实木加工利用技术的引进"(2000-04-13)
关键词
桉树
单板层积材
静曲强度
弹性模量
Eucalyptus
laminated veneer lumber(LVL)
modulus of rupture(MOR)
modulus of elastic(MOE)