聚丙烯酰胺辅助溶剂热法合成CdSe纳米线 被引量:1

Solvothermal Synthesis of CdSe Nanowires Assisted with Polyacrylamide
下载PDF
导出
摘要 通过溶剂热法,在180℃,利用聚丙烯酰胺辅助合成了直径约为20nm,长度为几百纳米到几微米的CdSe纳米线.通过XRD、TEM、HRTEM表征了产物的结构和形貌,并且讨论了反应时间对产物形貌的影响以及聚合物辅助纳米线生长的机制.通过紫外-可见光谱和光致发光光谱研究了纳米线的光学性能,在660nm处有一明显的吸收峰,与体相材料相比具有明显的量子尺寸效应. CdSe nanowires with an average diameter of 20nm and lengths of several hundreds of nanometers to several micrometers were synthesized by a solvothermal method assisted with polyacry- lamide (PAM) at 180℃. The structure and morphology of as prepared products were characterized by XRD, TEM and HRTEM. Also, the effect of reaction time on nanowire growth and the growth mechanism were discussed. The optical properties of CdSe nanowieres were investigated by UV-vis and fluorescence spectroscopy measurements. An absorption peak found at 660nm in the UV-vis spectrum indicates that the as-prepared CdSe nanowires show a strong blue shift due to quantum confinement effect
出处 《无机材料学报》 SCIE EI CAS CSCD 北大核心 2007年第5期838-842,共5页 Journal of Inorganic Materials
基金 国家自然科学基金(60471005)
关键词 CDSE 纳米线 溶剂热 聚丙烯酰胺 CdSe hanowires solvothermal polyacrylamid
  • 相关文献

参考文献22

  • 1Xu D S,Xu Y J,Chen D P,et al.Adv.Mater.,2000,12(7):520-522.
  • 2Alivisatos A P.Science,1996,271:933-937.
  • 3Peng X G,Manna L,Yang W D,et al.Nature,2000,404(6773):59-61.
  • 4Huang Y,Duan X,Wei Q,et al.Science,2001,291:630-633.
  • 5Koga T,Sun X,Cronin S B,et al.Appl.Phys.Lett.,1999,75:2438-2440.
  • 6Matt L,Lori E,Greenel J C,et al.Nature Materials,2005,4:455-459.
  • 7Whang D,Jin S,Lieber C M.Nano Letters,2003,3 (7):951-954.
  • 8Duan X,Huang Y,Cui Y,et al.Nature,2001,409(6816):66-69.
  • 9Jyongsik J,Mincheol C.Adv.Mater.,2005,17:1616-1620.
  • 10Sharmaa H,Sharmab S N,Singha G,et al.Physica E,2006,31 (2):180-186.

同被引文献16

  • 1滕枫,唐爱伟,高银浩,梁春军,徐征,王永生.水溶胶CdSe/CdS核/壳结构纳米晶制备及光学性质的研究[J].光谱学与光谱分析,2005,25(5):651-654. 被引量:22
  • 2王雪婷,于俊生,谢颖.水溶性CdSe/CdS量子点的合成及其与牛血清蛋白的共轭作用[J].无机化学学报,2007,23(7):1185-1193. 被引量:20
  • 3Liu J F, Li Q H, Wang T H, et al. Metastable vanadium dioxide nanobehs : hydrothermal synthesis, electrical transport, and magnetic properties [ J ]. Angew Chem Int Ed,2004,43 (38) : 5048 - 5052.
  • 4Fang X S, Xiong S L, Zhai T Y, et al. High-performance blue/ ultraviolet-light-sensitive ZnSe-nanohelt photodetectors [ J ]. Adv Mater,2009,21 (48) :5016 - 5021.
  • 5Jie J S, Zhang W J, Jiang Y,et al. Single-crystal CdSe nanoribbon field-effect transistors and photoelectric applications [ J ]. Appl Phys Lett,2006,89(13) :133118(3 pages).
  • 6Ji T H, Dong L Y, Liu Y, et al. Facile preparation of Ag-coated Ti02 nanobelts and their photocatalytic activities [ J ]. J Nanosci Nanotech,2011,11 (5) :3861 - 3866.
  • 7Gao T, Li Q H, Wang T I-I. CdS nanobelts as photoconductors [ J ]. Appl Phys Lett ,2005,86 ( 17 ) : 173105 -173107.
  • 8Liu Y K,Zapien J A,Geng C Y,et al. High-quality CdS nanoribbons with lasing cavity[ J]. Appl Phys Lett,2004,85 ( 15 ) : 3241 - 3243.
  • 9Huynh W U, Peng X G, Alivisatos A P. CdSe nanocrystal rods/poly (3-hexylthiophene) composite photovohaic devices [ J ]. Adv Mater, 1999,11 ( 11 ) :923 - 927.
  • 10Pan D C, Wang Q, Jiang S C, et al. Synthesis of extremely small CdSe and highly luminescent CdSe/CdS core-shell nanocrystals via a novel two-phase thermal approach[ J]. Adv Mater,2005,17 (2) :176 -179.

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部