摘要
结合鞍钢冷轧厂镀锌线投产三年来的生产实践,对热镀锌板锌渣缺陷形成机理进行了分析,重点探讨锌渣缺陷产生的原因,提出在实际生产中从工艺和设备上采取措施进行控制,减少锌渣缺陷的产生,提高镀锌板表面质量。
According to practice of galvanization line in cold rilling plant in Ansteel, the generating cause and mechanism of zinc slag defect on galvanization plate have been discussed and controlled. High quality galvanization plate has been manufactured after effect controlling.
出处
《上海金属》
CAS
2007年第5期87-90,共4页
Shanghai Metals
关键词
热镀锌
缺陷
锌渣
Hot Galvanization, Defect, Zinc Slag