The degradation of butanediamine-grafted poly（DL-lactic acid） polymers （BDPLAs） in vitro together with PDLLA and maleic anhydride-grafted poly（DL-lactic acid） polymers （MPLAs） was investigated by observation of the changes of the pH value of incubation media, and weight loss ratio during degradation duration of 12 weeks. The results reveal that the acidity of PDLLA degradation products was weakened or neutralized by grafting butanediamine onto PDLLA. A uniform degradation of BDPLAs was observed in comparison with an acidity-induced auto-accelerating degradation featured by PDLLA and MPLAs. The biodegradation behaviors of BDPLAs can be adjusted by controlling the content of BDA. BDPLAs might be a new derivative of PDLLA-based biodegradable materials for medical applications without acidity-caused irritations and acidity-induced auto-accelerating degradation behavior as that of PDLLA.
The degradation of butanediamine-grafted poly（DL-lactic acid） polymers （BDPLAs） in vitro together with PDLLA and maleic anhydride-grafted poly（DL-lactic acid） polymers （MPLAs） was investigated by observation of the changes of the pH value of incubation media, and weight loss ratio during degradation duration of 12 weeks. The results reveal that the acidity of PDLLA degradation products was weakened or neutralized by grafting butanediamine onto PDLLA. A uniform degradation of BDPLAs was observed in comparison with an acidity-induced auto-accelerating degradation featured by PDLLA and MPLAs. The biodegradation behaviors of BDPLAs can be adjusted by controlling the content of BDA. BDPLAs might be a new derivative of PDLLA-based biodegradable materials for medical applications without acidity-caused irritations and acidity-induced auto-accelerating degradation behavior as that of PDLLA.
基金
the National Natural Science Foundation of China(No.30470474)
the Chongqing Key Technologies R&D Program(No.CSTC2006AB4007)