摘要
A preferable honeycomb ceramics of Al2TiO5-TiO2-SiO2 doped by CeO2 and Er2O3 with high performance was prepared by means of extrusion molding and the effects of CeO2 and Er2O3 on the mechanical strength, thermal stability, and sintering temperature of ATS ceramics were mainly investigated. The experimental results and the microscopic analysis by scanning electron microscope, X-ray powder diffxaction, and TG-DSC showed that adding CeO2 and Er2O3 into ATS could prohibit the growth of their crystal grains and make their size uniform, which finally decrease its sintering temperature, and also enhance its mechanical performance as well as thermal stability. After the reforming, ATS doped by 0.5% CeO2 ＋0.5% Er2O3 was sintered at 1250 ℃, its bending strength reached to 177A MPa and thermal expansion coefficient was 3.8 ~ 10^-6/℃ at 25 - 1000℃, which provided a promising basis of making monolithic honeycomb catalyst of deNOx.
A preferable honeycomb ceramics of Al2TiO5-TiO2-SiO2 doped by CeO2 and Er2O3 with high performance was prepared by means of extrusion molding and the effects of CeO2 and Er2O3 on the mechanical strength, thermal stability, and sintering temperature of ATS ceramics were mainly investigated. The experimental results and the microscopic analysis by scanning electron microscope, X-ray powder diffxaction, and TG-DSC showed that adding CeO2 and Er2O3 into ATS could prohibit the growth of their crystal grains and make their size uniform, which finally decrease its sintering temperature, and also enhance its mechanical performance as well as thermal stability. After the reforming, ATS doped by 0.5% CeO2 ＋0.5% Er2O3 was sintered at 1250 ℃, its bending strength reached to 177A MPa and thermal expansion coefficient was 3.8 ~ 10^-6/℃ at 25 - 1000℃, which provided a promising basis of making monolithic honeycomb catalyst of deNOx.
基金
Project supported by National High Technology Research and Development Program of China (863 Program,2006AA02Z211)
Nation-al Natural Science Foundation of China (20376034)
Natural Science Foundation of Jiangsu Province (BK2006181)