摘要
采用原位聚合法制备了乙烯基酯树脂(VER)/苯乙烯-乙烯-丙烯(SEPS)嵌段共聚物复合材料,并用SEM、DSC等对其结构进行了表征,研究了组分变化对VER/SEPS的结构及其力学性能的影响。结果表明:原位聚合法制得的VER/SEPS复合材料具有互穿网络(IPN)结构;随着体系中SEPS含量的增加,最大拉伸强度呈下降趋势,断裂伸长率和冲击强度呈现上升趋势;当wSEPS<0.175,wVER=0.15时杨氏模量可提高约800%。
VER/SEPS composite with IPN structure was in-situ prepared and characterized via SEM and DSC. Effects of different components on the IPN structure of the composites were studiedin detail. The mechanical behavior of VER/SEPS composite was investigated and related to micro-structure. With the adding of SEPS, the impact strength and elongation at break show a risingtendency,but ultimate tensile strength decreases. When ωVER=0. 15 and ωSEPS〈0. 175, Young′modulus rises about 8 times than that of the sample without VER.