CO与Cs在Ru(101-0)表面上共吸附的高分辨电子能量损失谱研究结果表明:CO在有Cs覆盖的Ru(101-0)表面上有两种吸附状态,除了与CO在清洁表面上相似的一种吸附状态以外,还有一种新的吸附状态,它的C—O伸缩振动频率比前者低得多.在CO暴露过程中,CO分子首先吸附在低C—O伸缩振动频率的状态,随着CO覆盖度的增加,两种吸附状态的C—O伸缩振动频率都向高频方向移动.两种吸附状态的C—O伸缩振动频率也与Cs的覆盖度有关.当CO覆盖度饱和后。
Abstract CO+Cs/Ru(101-0) system has been investigated using HREELS. Two molecular adsorption states of CO were found. One with higher C—O frequency was similar to that on clean Ru(101-0) surface, while the other with lower C—O frequency appears on a Cs precovered Ru(101-0) surface. Two states of CO were occupied sequentially during the exposure to CO. The frequencies of both two loss peaks shift to higher values with exposure to CO and to lower values with higher Cs precoverage.