摘要
利用微波合成法将Ce和Ni引入到SBA-15分子筛骨架中。通过X射线粉末衍射(XRD)、傅立叶变换红外(FT-IR)、紫外可见漫反射(DRS)、透射电镜(TEM)和N2的等温吸附-脱附法等手段进行表征。结果表明,Ce和Ni物种进入SBA-15分子筛的骨架。将它作为催化剂载体,负载上Pt,以CO氧化为模型反应,考查催化剂的活性。结果表明,Pt/Ce-Ni-SBA-15催化剂的最低完全转化温度为227℃,与Pt/SBA-15相比,最低完全转化温度降低了39℃。说明了骨架掺杂后的Ce-Ni-SBA-15与SBA-15相比更有望成为更优良的催化剂载体。
.Ce-Ni-SBA-15 mesoporous molecular sieves was successfully synthesized by a microwave method, and characterized by X-ray diffractometer (XRD) , Infrared spectroscopy (FT-IR), DR ultraviolet and visible spectrophotometry (DRS), transmission electron microscope and low temperature N2 adsorption-desorption method. The result showed that the Ce and Ni were successfully incorporated into the framework of SBA-15 molecular sieves. Then the Ce-Ni-SBA-15 was loaded with Pt and applied in the CO oxidation reaction, and presences high catalytic activity. The result shows that the lowest complete conversion temperature of the CO on Pt/Ce-Ni- SBA-15 catalyst is 227℃, which is 39℃ lower than that of the Pt/SBA-15. Hence one can conclude that Ce-Ni- SBA-15 is a superior support for catalyst.
出处
《功能材料》
EI
CAS
CSCD
北大核心
2007年第10期1702-1704,1708,共4页
Journal of Functional Materials
基金
国家自然科学基金资助项目(20576021)
国家科技攻关计划资助项目(2005BA637C)
福建省教育厅资助项目(2005K015)