研究了雾化沉积ＳｉＣｐ／２０１４复合材料的时效行为。结果表明，在ＳｉＣｐ／２０１４的时效过程中，峰值时效的主要强化相为β相（Ｍｇ２Ｓｉ），其最佳的时效工艺为５０２℃固溶４０ｍｉｎ，１７０℃时效４．５ｈ。
In this paper,the process of aging precipitation in the spray formed Sicp/2014 composites was investigated The results show that the main precipitation phase of peak hardness is βphase (Mg 2Si),and its optimum process is solution treated at 502℃ for 40 min,aging at 170℃ for 4 5h