A new lead（Ⅱ） iodide coordination polymer [（npq）（PbI3）]n1 （npq = N-propyl- quinolinium） has been synthesized in the presence of npq as structure-directing reagent （SDA）. Compound 1 crystallizes in the orthorhombic system, space group Pbca, with a = 19.158（4）, b = 7.9909（16）, c = 22.929（5） A, V = 3510.2（12） A3, Z = 8, Dc = 2.877 g/cm3, F（000） = 2672, C12H1413NPb, Mr= 760.14, μ（MoKα） = 14.872 mm-1, the final R = 0.0431 and wR = 0.1021 for 3678 observed reflections with Ⅰ 〉 2σ（Ⅰ）. Structure determination indicates that the [PbI3]^-n infinite chains in each unit cell shape the sketch of 1, which could be described as the result of face-sharing distorted PbI6 octahedra running along the b axis. Electrostatic interaction between conjugated organic counter-cations and inorganic moieties presents and contributes to the crystal packing. 1 was further characterized with IR and elemental analysis. Based on the crystal structure data, quantum chemical calculation with DFT method was used to reveal the electronic structure and optical property of 1.
A new lead（Ⅱ） iodide coordination polymer [（npq）（PbI3）]n1 （npq = N-propyl- quinolinium） has been synthesized in the presence of npq as structure-directing reagent （SDA）. Compound 1 crystallizes in the orthorhombic system, space group Pbca, with a = 19.158（4）, b = 7.9909（16）, c = 22.929（5） A, V = 3510.2（12） A3, Z = 8, Dc = 2.877 g/cm3, F（000） = 2672, C12H1413NPb, Mr= 760.14, μ（MoKα） = 14.872 mm-1, the final R = 0.0431 and wR = 0.1021 for 3678 observed reflections with Ⅰ 〉 2σ（Ⅰ）. Structure determination indicates that the [PbI3]^-n infinite chains in each unit cell shape the sketch of 1, which could be described as the result of face-sharing distorted PbI6 octahedra running along the b axis. Electrostatic interaction between conjugated organic counter-cations and inorganic moieties presents and contributes to the crystal packing. 1 was further characterized with IR and elemental analysis. Based on the crystal structure data, quantum chemical calculation with DFT method was used to reveal the electronic structure and optical property of 1.
基金
the Special Foundation for Young Scientists of Fuzhou University (XRC-0644)
Sci & Tech Promotion Foundation of Fuzhou University (XJJ-0605)
Foundation of Education Committee of Fujian Province (JB06013)