摘要
The kinetics of ε-Cu particles dissolution in the matrix during welding of a copper-precipitation strengthening steel was determined by a combination of GleebleTM physical simulation, TEM examination and hardness meas urement. The ε-Cu particles underwent a coarsening and part dissolution and then complete dissolution reaction as the peak temperature increased from 750 to 1 000℃, which resulted in the decrease in the number density of ε-Cu particles and hardness in the heat affected zone （HAZ）. The results can be used to understand the evolution of this transformation and a softening behavior of the HAZ during welding of this type of steel.
The kinetics of ε-Cu particles dissolution in the matrix during welding of a copper-precipitation strengthening steel was determined by a combination of GleebleTM physical simulation, TEM examination and hardness meas urement. The ε-Cu particles underwent a coarsening and part dissolution and then complete dissolution reaction as the peak temperature increased from 750 to 1 000℃, which resulted in the decrease in the number density of ε-Cu particles and hardness in the heat affected zone （HAZ）. The results can be used to understand the evolution of this transformation and a softening behavior of the HAZ during welding of this type of steel.
基金
National Basic Research Program(G1998060101507)