The present study aims at finding out the effect of the addition of a single rare earth element, that is, lanthanum on the nodularity and nodule count of ductile iron under controlled conditions. For this purpose, four melts with different compositions were made, using a 28 kg inductotherm medium frequency induction furnace. The temperature was carefully maintained between 1400 and 1450 ℃ for these heats. A good quality charge consisting of Sorel metal, ferrosilicon, Swedish iron, ferrosilicon magnesium, and ferrosilicon lanthanum was used for the production of melts. A vertically parted sand mould was used for casting of 10 test bars made from local silica sand. Standard coin samples were chill-cast to conduct chemical analysis of the ductile iron. Mierostructure study of the samples was conducted using a Leica optical microscope. Nodule count and nodularity of the samples were carried out using an image analyzer. The results obtained indicated that with the increased addition of lanthanum the nodule count of ductile iron increased, thus making it evident that it played a significant role in increasing the mechanical properties. The highest nodule count of 467 was obtained with the addition of 0.03% lanthanum. However, the effect of lanthanum on nodularity was negligible with nodularity ranging from 81% to 83 %.
The present study aims at finding out the effect of the addition of a single rare earth element, that is, lanthanum on the nodularity and nodule count of ductile iron under controlled conditions. For this purpose, four melts with different compositions were made, using a 28 kg inductotherm medium frequency induction furnace. The temperature was carefully maintained between 1400 and 1450 ℃ for these heats. A good quality charge consisting of Sorel metal, ferrosilicon, Swedish iron, ferrosilicon magnesium, and ferrosilicon lanthanum was used for the production of melts. A vertically parted sand mould was used for casting of 10 test bars made from local silica sand. Standard coin samples were chill-cast to conduct chemical analysis of the ductile iron. Mierostructure study of the samples was conducted using a Leica optical microscope. Nodule count and nodularity of the samples were carried out using an image analyzer. The results obtained indicated that with the increased addition of lanthanum the nodule count of ductile iron increased, thus making it evident that it played a significant role in increasing the mechanical properties. The highest nodule count of 467 was obtained with the addition of 0.03% lanthanum. However, the effect of lanthanum on nodularity was negligible with nodularity ranging from 81% to 83 %.