Ni-mSA-mCS bipolar membrane （BM） was prepared by sodium alginate （SA） and chitosan （CS）, which were modified by Ca^2＋ and glutaraldehyde as linking reagents, respectively, mSA-mCS membrane was characterized by FTIR, SEM, TG and used as a separator in the electrolysis cell to produce thioglycolic acid （TGA）. The experiment results show that TGAwas prepared effectively by electro-reduction of dithiodiglycolic acid （DTDGA） with the mixture of TGA and DTDGA in the cathodic chamber. The current efficiency was up to 66.7% at the room temperature （25 ℃） during the current density of 10 mA/cm^2. Compared with the traditional metal reduction method, the electro-reduction technology saves the zinc powder and eliminates the pollution to environment.
Ni-mSA-mCS bipolar membrane （BM） was prepared by sodium alginate （SA） and chitosan （CS）, which were modified by Ca^2＋ and glutaraldehyde as linking reagents, respectively, mSA-mCS membrane was characterized by FTIR, SEM, TG and used as a separator in the electrolysis cell to produce thioglycolic acid （TGA）. The experiment results show that TGAwas prepared effectively by electro-reduction of dithiodiglycolic acid （DTDGA） with the mixture of TGA and DTDGA in the cathodic chamber. The current efficiency was up to 66.7% at the room temperature （25 ℃） during the current density of 10 mA/cm^2. Compared with the traditional metal reduction method, the electro-reduction technology saves the zinc powder and eliminates the pollution to environment.
基金
supported by the Nature Science Foundations of Fujian Province(No.D0710009)
the Fujian Education Bureau(Nos.JB06069,JB05314).