摘要
在制砖基料中加入20%铬渣,制成所要求几何形试块,按给定的烧成温度烧成试块,测量烧成试块几何尺寸及烧成前后试块所含水溶性Cr(Ⅵ)值.将烧成试块置于不同条件的浸出液中进行长期浸取.根据1a的浸出数据,浸出率LR=0.8×10-7cm/d,累积浸出分数LF=1×10-4cm,判断炻质砖试块中Cr(Ⅵ)的稳定程度。
By adding 20% chromium bearing slag into base materials of making brick, the brick sample was sintered in the required geometric shape under the given temperature. The size of sintered base sample was measured and the associated Cr water solubility test made before and after sintering. The sample was tested in leaching liquid under variable conditions. Based on the experiment results data,the leaching rate is 0.8×10 -7 cm/d and the accumulative leaching faction is 1×10 -4 cm/d, the stability of Cr in base sample was determined and therefore such method of treating chromium slag was considered feassible and practible.
出处
《环境科学》
EI
CAS
CSSCI
CSCD
北大核心
1997年第3期54-56,共3页
Environmental Science
基金
国家"八五"重点科技攻关项目
关键词
铬渣
炻质砖
六价铬
稳定性
chromium bearing slag,road tile, stability.